Refurbished turbine components, such as vanes or blades

ABSTRACT

A refurbished turbine vane or blade. Used turbine vanes and blades are cleaned, annealed and in some cases slotted adjacent their ends, after which any cooling passages are welded closed and all cracks welded over, on both leading and trailing edges. The trailing edge, for a vane or blade having a short chord, is built up by welding along its full length with an alloy wire, after which any slots that were cut adjacent the ends are closed, also by welding. Then the worn surfaces of the vane or blade are built-up by a plasma spray process, using a metal powder with added silica, to a thickness as great as 30 to 40 thousandths of an inch. The built-up vane or blade is then sintered and thereafter surface finished to conform to the original contour of the component when new. Any cooling holes are finally recut, and the vane or blade polished as required and inspected.

CROSS REFERENCES TO RELATED APPLICATIONS

This application is a division of our co-pending application Ser. No. 613,479 filed Sept. 15, 1975, now U.S. Pat. No. 4,028,787 dated June 14, 1977, and entitled REFURBISHED TURBINE VANES AND METHOD OF REFURBISHMENT THEREOF.

Application for U.S. Letters Patent on METHOD AND MEANS FOR REPAIRING TURBINE VANES in the name of Ralph T. DeMusis, Ser. No. 528,839, filed Dec. 2, 1974, now abandoned.

BACKGROUND

This invention relates to the recovery of worn turbine components, and more particularly to the reworking and resurfacing of worn vanes or blades so as to extend the useful life thereof.

Heretofore turbine vanes and blades as used in aircraft engines, power stations and the like have had a specific useful life, after which they were removed and discarded as being no longer capable of service. Since the initial cost of such components is quite considerable, this practice resulted in an appreciable expense that was involved with the maintenance of the turbines. In addition to the loss of use of the equipment involved and the expense of labor in installing new vanes, there was the additional very considerable outlay required for the new replacement parts, either blades or vanes, which were to be installed. This prior practice, which was necessary to maintain the equipment in reliable operating condition, therefore resulted in high operating charges.

SUMMARY

The above disadvantages and drawbacks of prior costly procedures for maintaining turbines and like equipment are in large part obviated by the present invention, which has for its main object the provision of improved, acceptable refurbished vanes and blades by which there is considerably reduced the maintenance costs involved with wear and attrition of turbine engines. A related object of the invention is to provide improved, refurbished vanes and blades for turbines, wherein the resultant product can meet rigid requirements of strength and performance, readily acceptable for the fields of service involved. A still further object of the invention is to provide improved refurbished vanes and blades which can be produced at a relatively low cost.

The above objects are accomplished by a procedure which first welds closed all cracks, pitted areas and the like, and in some cases slots end portions of the vane or blade component, then builds up, by welding, the trailing edge of the vane or blade to at least the original dimension. Where considered necessary, bead reinforcements are welded, positioned coextensive with and spaced from the trailing edge on both sides of the vane or blade, after which the worn surfaces of the components are built-up by a plasma spray process using powdered metal with added silica, which latter burns off during the spraying procedure. Any slotting of the vanes or blades prior to appreciable build-up of the surfaces can be done to prevent distortion; the slots are welded closed, together with any cooling passages, before the application of the molten plasma-sprayed metal. Finally, the airfoil surfaces are recut to conform to the original contours, and any cooling holes are then cut through as per original specifications.

Where slotting is done to relieve stresses, or a lateral reinforcement effected by positioned welding beads, the welding of all cracks and subsequent metal build-up by plasma spraying results in a high quality refurbished product which meets the essential service requirements originally specified for new vanes or blades. The alloy metal which is added to the components to build up the worn surfaces conforms to the original metallurgy, by virtue of the use of additional silica to the metal powder used in the plasma spraying, such silica burning off in the plasma stream.

Other features and advantages will hereinafter appear.

In the accompanying drawings:

FIG. 1 is an elevational view of the convex side of a vane of the type refurbished by a process involved with the invention.

FIG. 2 is an elevational view of the concave side of the vane.

FIG. 3 is a cross-section through the vane, taken on the line 3--3 of FIG. 1.

FIG. 4 is a section taken on the line 4--4 of FIG. 2.

FIG. 5 is a fragmentary cross-section showing a portion (designated by the lines X--X) of FIG. 3 greatly enlarged.

FIG. 6 is an elevational view of the convex side of a worn vane. This view is similar to the showing of FIG. 1 but illustrates certain steps in the processing of the component.

FIG. 7 is an elevational view of the concave side of the vane of FIG. 6, showing other steps and welded beadments as incorporated on the vane prior to the plasma spraying.

FIG. 8 is a cross-section through the vane, taken on the line 8--8 of FIG. 6.

FIG. 9 is a side elevational view of a plasma spray gun, shown applying a coat of molten metal to one surface of a turbine vane.

FIG. 10 is a perspective fragmentary view of a grinding apparatus for removing controlled quantities of the built-up surface of the vane, to therefore restore the airfoil surface of the vane to its original dimensions.

Considering first FIGS. 1-4, a finished or refurbished component in the form of a vane designated 10 is shown, said vane comprising convex and concave airfoil portions 12, 14 joined at a broad leading edge 16 and also at a narrow trailing edge 18. The vane 10 is hollow, having an airfoil-shaped inner space 20 between the airfoil portions. Adjacent the trailing edge 18, the vane 10 has cooling passages 22 which communicate with the interior space 20. Such passages are clearly seen particularly in FIG. 2.

The vane 10 of FIGS. 1-4 has been refurbished according to the process by which the invention is carried out, and in FIGS. 3 and 4 the cross-sectional areas 24 designate overlay metal which has been added to the vane surfaces by a plasma spray process and thereafter refinished to conform to the original contours as specified for new vanes. The overlay metal of the areas 24 can be applied to build up a thickness of as much as 30 to 40 thousandths of an inch, and can be feathered as shown, as the overlay approaches the trailing edge 18 of the vane.

We have found that vanes which have their surfaces built-up by a plasma spray procedure according to the process by which the invention is carried out meet rigid requirements for reuse, and are capable of an extended useful operative life.

The application of the overlay metal is such that the resultant alloy closely conforms to the alloy of the base metal of which the vane was originally cast. This is accomplished by the use of additional silica in the metal powder used in the plasma spraying. We have found that by the addition of 10% of silica to the powdered alloy, the burn-off of silica during the plasma spraying is such that the resultant alloy of the overlay can be made essentially the same as the alloy of the base metal. The base metal alloy of vanes refurbished by the invention can be that known commercially as Haynes Alloy #25, or #31, having a composition given by the table below.

ESSENTIAL CHEMICAL ANALYSIS OF HAYNES ALLOY #25

Parts by weight:

    ______________________________________                                         1.        Carbon          .09                                                  2.        Silicon         .22                                                  3.        Manganese       1.55                                                 4.        Phosphorus      .018                                                 5.        Sulfur          .007                                                 6.        Chromium        20.32                                                7.        Nickel          10.56                                                8.        Tungsten        14.30                                                9.        Iron            2.25                                                 10.       Cobalt          50.685                                               ______________________________________                                    

The above alloy is also used in various welding procedures on the vanes as described below, being supplied in the form of welding rod or wire known commercially as type L-605.

For the plasma spraying of the overlay metal, the Haynes alloy as above constituted is used in the form of a metal powder to which there is added 10% silica. During the plasma spraying, the heat of the process burns off essentially the 10% additional silica whereby there remains the original alloy having a composition as set forth by the above table.

We have found that the bond between the base metal 12, 14 and overlay 24 in consequence is especially strong and durable, and not likely to fail during use of the vane.

The process of refurbishing vanes, starting with used, worn components is essentially as follows:

Referring to FIG. 6, a vane to be refurbished according to the invention, as exemplified by one embodiment thereof, is cut to provide a pair of slits 26 adjacent the end flanges 28, said slits being made from the trailing edge 18 substantially parallel with the end flanges and for a distance roughly as shown in the figure. The slits 26 are made, where required, to relieve stresses caused by any unequal heating of the vane during the processing. After formation of any slits 26, a welded bead 30 can be applied to the trailing edge, in cases where the chordal distance (from the leading edge) has become shotened by wear. Also, welded repairs indicated as short beads 32 are made to the leading and trailing edges to fuse over any hairline cracks. A pair of beads 34, 36 (formed by welding worn areas of the convex and concave surfaces respectively) are provided in those instances where the vanes are badly worn, to reinforce the vane airfoil structure, such beads extending in spaced relation to the trailing edge 18 and substantially coextensive therewith.

Also, as seen in FIG. 7, any air cooling passages 22 of the vane are welded closed by beads 40. Finally, the slots 26 are welded closed by beads 42. Thereafter, following any surface processing that is employed, the airfoil surfaces are plasma sprayed to deposit a layer of alloy metal 24 indicated by the broken outline in FIG. 8. The layer 24 which is the built-up surfacing done by plasma spraying, can be as thick as from 30 to 40 thousandths of an inch, tapering to feathered edges as the trailing edge 18 of the vane is approached. Prior to the plasma spraying build-up, a surface processing of the vanes is carried out, in the form of a sand blast, or shot peen.

The showings of FIGS. 6-8 illustrate steps in the preparation of a worn vane, prior to building up the surfaces by spraying of the molten metal in a plasma.

A complete procedure involving a process associated with the invention, as exemplified by one embodiment thereof is as follows:

1. The used vanes are stripped of dirt, oil, etc. by placing them in a hydrochloric acid bath for 3 to 4 hours at a temperature of 180° F.

2. Thereafter, the vanes are rinsed in clear water and then vacuum annealed for 2 hours at a temperature of 2,175°.

3. The annealed vanes are then visually inspected.

4. After passing visual inspection they are Zyglo inspected by means of a fluorescent penetrant.

5. The vanes may then be slotted approximately one inch deep, starting at the trailing edges, the slots being located about 1/4 inch from the ends.

6. The air cooling holes are welded closed.

7. All cracks on the airfoil leading edge and trailing edge are welded.

8. If the trailing edges of the vanes are worn thin, they are built-up by welding, preferably using a Tungsten Inert Gas process, with Haynes #25 welding rod.

9. Convex and concave surfaces of the vane body adjacent but spaced from the trailing edge and coextensive therewith are reinforced by being built-up, involving placement of welding beads thereon, preferably using a Tungsten Inert Gas process. The beads can be as high as from 30 to 40 thousandths of an inch.

10. Any slots that were made adjacent the two ends of the airfoil surfaces are welded closed and the surface conditioned by roughening and cleaning with a sand blasting or shot peening operation.

11. The worn airfoil surfaces are then plasma sprayed with metal alloy powder having added silica, to a thickness of from 30 to 40 thousandths at the leading edges, and tapering to feathered edges as the trailing airfoil edges are approached. Where the vanes have been originally cast with an alloy such as Haynes #25 Alloy (the composition of which is given above), the powdered metal used in the plasma spraying is also of the same alloy composition and additionally has added silica, preferably in the amount of 10% additional.

12. The vanes after being thus built-up, are sintered in a vacuum or hydrogen furnace (5 microns) at 2,200° F. for one hour, and then furnace cooled.

13. The built-up airfoil surfaces are now recut by an abrading process, such as one using an abrasive belt, to produce the original surface measurements. The refinishing is preferably accomplished by an automatic machine employing an endless abrasive belt as described and claimed in the copending application of Ralph T. DeMusis identified above.

14. The vanes are then inspected by a Zyglo process.

15. The air cooling holes are recut by a laser beam, as per original specifications.

16. The vanes are then hand polished as may be required.

17. Finally the vanes are inspected for accuracy of dimension.

The process as set forth above has been successfully carried out, and the resultant refurbished vane product has passed rigid tests, where the vane metal has been that known commercially as Haynes #25 Alloy, whose composition is given in the table herein.

FIG. 5 pictures a photomicrograph of a section through a refurbished vane, taken at the location generally designated in FIG. 3 between the broken lines X--X. The designation of FIG. 5 represents an enlargement or magnification of approximately 100 times. The section of overcast metal 24, having been etched, reveals a dense grain structure which is joined to the roughened surface of the vane airfoil portion 14 at an interface 46. Such roughened surface is the result of sand blasting or ball-peening the vane in preparation for the plasma spray overcast. The vane airfoil portion 14 is shown conventionally by the usual cross-hatching lines. The use of cross-hatching in the overlay 24 is considered not desirable since the cross-section surface has been etched to reveal grain structure and grain lines are of more importance. It will be seen that the grain structure of the overlay 24 is characterized by a desirable uniformity, as the section is traversed from the outer surface to the interface 46. The uniformity and the density of the plasma spray coating is important in providing for uniform wear or attrition when the vane is in use, with an absence of porous or soft spots which could break down quickly.

Turbine components such as vanes refurbished in accordance with our invention as explained above were tested as to the bond strength of the plasma sprayed overlay or recast material on the airfoil surfaces. It was found that the plasma spray deposit is uniform and of high density. Also, the bond between the overlay material and the base metal was excellent, with no evidence of separation at any points around the periphery of the airfoil. A spectro-chemical analysis of the overlay material revealed a cobalt based alloy of the Haynes Alloy #25 type. Moreover, the overlay material was capable of being successfully coated with oxidation and sulfidation-resistant alloys. The strength of the overlay to base metal bond was equivalent or superior to conventional plasma spray type deposits.

The cost represented by the refurbishment process, while significant, constitutes a small fractional value of the initial cost of producing turbine components, such as blades or vanes or this type. The resultant refurbished product meets the essential high quality standards set for new turbine components, and accordingly the present invention constitutes a distinct advance and improvement in the art.

Each and every one of the appended claims defines a distinct aspect of the invention separate from the others, and each claim is accordingly to be treated in this manner when the prior art devices are examined in any determination of novelty or validity.

Variations and modifications are possible without departing from the spirit of the invention. 

We claim:
 1. A refurbished turbine component comprising, in combination:(a) a component structure having opposite contoured convex and concave airfoil faces, said component structure including mounting flanges at opposite ends of said airfoil faces, (b) said component structure having welded-over portions at places where cracks have appeared along the trailing edge, (c) the leading edge of said component structure and said convex and concave airfoil faces having a plasma-sprayed, build-up metal overlay which tapers in thickness as the trailing edge of the component is approached.
 2. A refurbished turbine component as in claim 1, wherein:(a) the trailing edge of the component structure has welded portions which extend said edge a distance further from the leading edge.
 3. A refurbished turbine component comprising, in combination:(a) a metal component structure having opposite contoured convex and concave airfoil faces, said component structure including mounting flanges at opposite ends of said airfoil faces, (b) said component structure having welded-over portions at places where cracks have appeared along the trailing edge, (c) said component structure having a reinforcing welded portion on one of its airfoil faces, spaced from and substantially coextensive with the trailing edge, and having welded portions at the ends of the convex and concave airfoil faces, extending along and closely adjacent the mounting flanges and for a distance inward from the trailing edge thereof, (d) the leading edge of said component structure and said convex and concave airfoil faces having a plasma-sprayed, built-up metal overlay which tapers in thickness as the trailing edge of the component is approached.
 4. A refurbished turbine component as in claim 3, wherein:(a) the other of said airfoil faces has welded portions spaced from and extending substantially coextensive with the trailing edge of the component structure.
 5. A refurbished turbine component as in claim 1, wherein:(a) the concave airfoil face of the component structure has a plurality of welded portions disposed in a row along and spaced from the trailing edge thereof, and has passages extending through said welded portions from the concave airfoil face to a hollow of the component structure. 